摘 要
焊接是指通过加热或加压，或两者并用，并且视情况采用填充材料，使焊件达到原子间结合的一种方法。焊接在现实中应用很广泛，并且是一项很关键的工艺。它不仅对建造质量有影响，而且对生产率的提高、周期的缩短有很大作用。本文对Q345钢板的焊接性能进行化学分析、焊接试验、力学性能检测、金相分析、维氏硬度测试仪检测和无损检测等一系列的试验及研究。试验结果表明Q345钢板不仅有好的力学性能,还具有良好的焊接性能。
关键词 Q345 焊接试验 焊接检验{压焊论文}.
Abstract{压焊论文}.{压焊论文}.
Welding is to point to by heat or pressure, or both and use, and depending on the situation with filling materials, make the weldment between atoms combine a method.Welding is widely used in the reality, and is a very key technology.It not only have an effect on construction quality, and the improvement of productivity, cycle shorten has great effect.In this paper, the Q345 steel plate welding performance for chemical analysis, welding test, mechanical property testing, metallographic analysis, vickers hardness tester and nondestructive testing and so on a series of test and research.The experimental results showed that Q345 steel plate not only has good mechanical properties, but also has good welding performance.
Keywords Q345 welding test welding inspection
目 录
1 引言 ............................................................................................................................................. 1
2 焊接技术 .................................................................................................................................... 1
2.1焊接方法 ........................................................................................................................ 1
2.2焊接种类 ........................................................................................................................ 2
3 试验条件 .................................................................................................................................... 3
4 试验结果及分析 ...................................................................................................................... 3
4.1 Q345钢的理化性能 .................................................................................................... 3{压焊论文}.
4.2 Q345钢板焊接试验 .................................................................................................... 4
4.2.1埋弧焊方法 ......................................................................................................... 4
4.2.2焊接前准备 ......................................................................................................... 4
4.2.3焊接工艺参数的选择 ....................................................................................... 5
4.2.4焊接操作过程 ..................................................................................................... 5
4.2.5 Q345钢的焊接性 .............................................................................................. 6
4.2.6 Q345钢板及焊接接头金相组织 ................................................................... 7
4.2.7维氏硬度检测 ................................................................................................... 10
4.2.8 Q345钢无损检测 ............................................................................................ 12
结 论 ........................................................................................................................................... 15{压焊论文}.
致 谢 ........................................................................................................................................... 16
参 考 文 献 ............................................................................................................................... 17{压焊论文}.
1 引言
在金属加工工艺中,焊接是一门年轻但是又发展很快的一种加工工艺,目前以发展成为了一门独立的学科,并在能源、交通、修建，特别是在机械制造部门中得到广泛的应用。
Q345钢属16Mn系列钢种,平常在热轧状态下利用,它具备杰出的综合力学机能、较高的韧性、耐蚀性及焊接机能和冷成型本领,在我国获得广范的利用,可以用来制造大型船舶、桥梁、管道、汽锅、压力容器、煤油储存罐、起重机械、厂房钢架等承载负荷的焊接布局,这就需要它不但要有好的力学机能，还要有好的焊接机能。
伴随着我国钢铁企业竞争的日趋剧烈,钢铁产物的种类和质量将成为钢铁企业发展的重要题目。Q345、16MnL、16MnR、16Mnq、16Mng等公司所生产的16Mn系列钢板。当今, 多达上百种的焊接方式在工业生产获得利用,就焊接进程而言可分为三大类：熔焊、压焊、钎焊。由于客户要求16Mn系列钢板必须要具有良好的焊接性,为适应市场发展需要,公司生产的16Mn系列钢不但要满足一般的性能的需要,而且要满足用户对焊接性能的需要,因此,我们首先对Q345钢板进行了焊接性试验研究。
2 焊接技术
2.1焊接方法
当今, 多达上百种的焊接方式在工业生产获得利用,就焊接进程而言可分为三大类：熔焊、压焊、钎焊。
1) 熔焊
把焊接处的母材熔化为焊缝的体例叫作熔焊。要实现熔焊的关键在于要有一个局部热源，而这个局部热源要汇合很大的能量、温度足够高的。依照所利用的热源的分歧，熔焊又可以分为如下几种方式：电弧焊、气焊、铝热焊、电渣焊、电子束焊、激光焊等多少种。
在熔焊时，为了制止焊接区的高温金属与周边空气的相互作用从而让其性能使之恶化，在焊接时要施加防护。而在平常事件中有造渣、通庇护气和抽真空三种庇护方式。